AST M A487 - 4B材料大截面试块机械性能研究及应用

3 蒋春宏 (兰州石油机械设备有限公司 ,甘肃 兰州 730050) 摘要:按照 API规范生产泥浆泵曲轴铸件 ,必须进行大截面试块机械性能的材料评定.

通过优化化学成分 ,介绍采用钢包底吹氩精 炼方式 ,不断调整热处理工艺 ,特别是亚温淬火的实施 ,保证了材料评定要求的机械性能. 关键词 :试块 ;

成分匹配 ;

精炼 ;

淬火 ;

性能 中图分类号 : TG162 文献标识码 : A 文章编号 :

1007 -

4414 (2006)

02 -

0023 -

02 Research and application for m echan ical property of large section coupon on ASTM A487 - 4B alloy steel Jiang Chun - hong (Lanzhou petroleum & m achinery equipm ent Co . , L td, Lanzhou Gansu 730050, China) Abstract: To produce Mud Pump castings per AP I specification, the material must carry out material qualification of large section coupon mechanical property . W e pass through fining chem ical composition. U sing blowing argon refining at ladle bot2 tom, adjusting heat treatment continuously, especially sub - temperature quench carried out, so that required mechanical property get meet for material qualification. Key words: coupon;

mating chem ical composition;

refining;

quench;

mechanical p roperty 我厂主要为 NOW (NationalO ilW ell美国国民油井公司 )提 供配套铸钢件 ,其中泥浆泵曲轴铸件根据美标规范 ,采用 AST M A487 - 4B承压钢材料 ,不仅内外质量需求高 ,且验收按 15″ * 15″ * 5″ 大截面试块的机械性能 ,特别是 - 20℃ 的夏比冲击值要 求达到 42J,常规铸造、 冶炼、 热处理工艺难以保证.笔者通过 改善铸造组织 ,提高其淬透性作为主要工艺手段来达到机械 性能的研发概况进行评述.

1 试验内容 1.

1 材料 材料选用 AST M A487 - 4B承压钢规范 ,并进行调整. (1) 确定材料化学成分 表 1为材料化学成分数据. (2) 性能检验 性能要求. 表1材料化学成分 C Mn Cr Ni Mo Si P≤ S≤ 0. 23~0.

28 0. 70~1.

00 0. 40~0.

80 0. 40~0.

80 0. 15~0.

30 0. 30~0.

60 0.

025 0.

025 按照采购规范 MS -

3144 (MS - 7144)要求 : σs: ≥85KPSI(586MPa) σb : ≥105KPSI(724MPa) δ

4 : ≥17%ψ: ≥35% HB:

217 -

269 冲击 : ( - 20℃)夏比"V " AKV≥42J (单个试样 ≥32J) 检验取样 按照 AST M E8规范 ,拉伸试棒直径选用