????? 微量Nd的添加对Mg-Al-Zn合金微观组织和高温力学性能的影响# 许春香,李威,周杨,王振强,刘艳萍**|1|许春香|XU Chunxiang|太原理工大学材料科学与工程学院,太原 030024|School of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024|许春香(1964-),女,教授,博士,主要研究方向:高强度耐热镁合金的研究|山西省太原市迎泽西大街79号3251信箱|030024|liv393@163.

com|0351-6010021|15536012966*|2|李威|LI Wei|太原理工大学材料科学与工程学院,太原 030024|School of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024|李威(1984-),男,硕士,主要研究方向:高强度耐热镁合金的研究|山西省太原市迎泽西大街79号3251信箱|030024|liv393@163.com|0351-6010021|15536012966|3|周杨|ZHOU Yang|太原理工大学材料科学与工程学院,太原 030024|School of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024|||||||4|王振强|WANG Zhenqiang|太原理工大学材料科学与工程学院,太原 030024|School of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024|||||||5|刘艳萍|LIU Yanping|太原理工大学材料科学与工程学院,太原 030024|School of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024||||||微量Nd的添加对Mg-Al-Zn合金微观组织和高温力学性能的影响|Effects of Nd on microstructure and mechanical properties at elevated temperature of Mg-Al-Zn alloy|山西省自然科学基金项目(2007011067);

山西省教育厅基金(20080010) (太原理工大学材料科学与工程学院,太原 030024) 摘要:通过金相显微镜等手段分析研究了微量Nd的添加对Mg-Al-Zn合金显微组织和高温力学性能的影响.结果表明:Nd的加入,显著细化了合金的铸态组织,同时出现了新相Al3Nd化合物.当Nd添加量为1.0%时,可使铸态Mg-8.5Al-0.5Zn合金150℃高温下的抗拉强度达到最大值为160MPa. 关键词: 镁合金;

钕;

显微组织;

力学性能 中图分类号:TG 146.22 Effects of Nd on microstructure and mechanical properties at elevated temperature of Mg-Al-Zn alloy XU Chunxiang, LI Wei, ZHOU Yang, WANG Zhenqiang, LIU Yanping (School of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024) Abstract: The microstructure and mechanical properties of Mg-Al-Zn magnesium alloys with Nd addition have been studied using optical microscopy (OM). The results show that Nd addition can significantly refine as-cast microstructure of Mg-Al-Zn magnesium alloys as well as results in formation of Al3Nd phase. When Nd addition was 0.1 wt.%, the tensile strength of cast alloys reach to the highest points at elevated temperature of 150℃, whose figures are 160MPa. Key words: Magnesium alloys;

Nd;

microstructure;

mechanical properties 引言 镁合金是最轻的商用金属工程结构材料之一,具有铝和钢不可替代的性能,如高比强度、高比弹性模量,高阻尼减震性、高导热性、高静电屏蔽性、高机械加工性、尺寸稳定性及极低的密度,特别是利于回收利用,具有环保特性,近年来在汽车、电子通讯工业及航空航天等领域的应用前景广泛[1-3]. 由于AZ系镁合金中在α-Mg晶界呈网状分布着的β相Mg17Al12对镁合金的力学性能有不利影响,因此在α-Mg晶界上形成热稳定性更高的新相或改善β相Mg17Al12的分布是提高AZ系合金高温性能的有效途径.本文研究了不同含量的Nd对Mg-8.5Al-0.5Zn合金显微组织和高温力学性能的影响及变化规律. 实验方法 试验所用的合金由纯镁、纯铝、纯锌、纯钕颗粒和Al-10%Mn中间合金熔炼而成,其具体化学成分见表1.熔炼在SG2-5-12型井式坩埚电阻炉中进行,坩埚材料为低碳钢.为防止合金氧化,在试验过程中采用RJ-6号熔剂作覆盖剂.合金在720℃熔炼,700℃时将镁合金液浇注到预热至200℃的金属模具中.在距铸棒底部15mm处截取试样,然后磨制、抛光,用3.5%硝酸酒精腐蚀.采用XJ-16A金相显微镜观察合金组织形貌,并采用JSU-6700F扫描电镜分析镁合金相结构形貌,采用Y-2000的X射线衍射分析仪对合金的相组成和相对含量进行分析,采用DNS100型电子万能试验机测量合金的拉伸力学性能. 表1试验用合金的化学成分 w(%) Table