1 B02.

生态环境材料 分会主席:聂祚仁,张忠伦 B02-01 基于多金属协同效应的锰基类芬顿催化剂的设计和结构调控 于岩 福州大学 B02-02 用于二氧化碳捕集的固态胺吸附剂材料的设计及其研究进展 陈水挟,何辉,刘风雷,王烁宇 中山大学 B02-03 Photocatalytic properties of BiOCl nanomaterials for environmental purification 王聪,王天民 北京航空航天大学 It was found that Bi-based nanomaterials displayed high photocatalytic activities under visible light irradiation, such as Bi2O3, Bi2WO6, BiVO4, BiOX(X=Cl, Br, I), etc.. We report the synthesis and photocatalytic properties of BiOCl powder and thin film, composited with Bi2WO6, CsxWO3 or AgCl, prepared by simple sol-gel method, incorporated with anode aluminum oxide (AAO) template or magnetron sputtering. Photocatalytic properties were evaluated by degradation of rhodamine B (Rh B), antiepileptic drug carbamazepine (CBZ) and other pollutants under visible light irradiation. The photocatalytic activities of black BiOCl and the composites BiOCl/ Bi2WO6, BiOCl/ AgCl, BiOCl/ CsxWO3 were shown to be much enhanced compared with pure BiOCl. In summary, crystal structure, crystallinity, morphology including specific surface area should be taken into consideration for improving photocatalytic activity. B02-04 废弃混凝土资源化工艺技术研究 冯庆革 1,2 ,张小利

1 ,李浩漩

1 1.广西大学资源环境与材料学院 2.广西高校环境保护重点实验室 随着城市化进程不断加快,房屋的拆除、新建以及改扩建项目不断增多,产生了大量的建筑垃圾;

在建筑垃圾中最大的组分就 是废弃混凝土,其中石灰石质粗骨料废弃混凝土数量最大.本研究通过对目前废弃混凝土的产生和再生利用技术进行了分析,并针 对存在的问题,提出了:1)制备高品质再生骨料的机械剥离工艺技术;

2)全组分废弃混凝土磨细粉,并作为水泥混合材使用. 研究结果表明:1)提出了使用机械剥离设备的处理新工艺;

利用机械剥离处理

10 min 内,获得的 5~20 mm 再生粗骨 料级配良好,且粒型得到较大的改善,针片状含量小于 4%;

吸水率达到 3.0%~6.0%,表观密度约为 2590~2640kg・m-3,压 碎指标基本处于 9.9%~16.4%范围内, 且回收率可以达到 37%;

各组再生细骨料属于粗砂区粒径范围, 细度模数约为 3.15~3.50, 吸水率均大于 5.0%,表观密度约为 2500~2550kg・m-3;

(2)提出的石灰石质再生骨料表面附着砂浆含量测试方法可行,经 测定发现,机械剥离处理对降低骨料表面砂浆含量有较好的效果,处理后砂浆含量约为 20~40%左右;

同时,再生骨料砂浆 含量不仅取决于生产工艺,还与原生混凝土的骨料性质及配合比有密切关系,且与其吸水率有相对应的关系;

(3)机械剥离 处理后